COMPARATIVE IN VITRO ASSESSMENT OF BLACK AND GREEN TEA EFFECTS ON THE CORROSION AND MECHANICAL INTEGRITY OF ORTHODONTIC WIRES

Wurood khairallah Al-Lehaibi*, Abdulrahman Al-Najjar, Faehaa Al-Mashhadane

Department of Prevention, Orthodontic, Pedodontic dentistry, dentistry department, Dijlah university College, Iraq. · Department of Dental Basic Science, College of Dentistry, University of Mosul, Mosul, Iraq.

Received: 2025-09-17 · Published: 2025-09-12

© 2025 The Author(s) and the original publisher.

CC BY-NC 4.0 This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.
Shared article.
Original title
COMPARATIVE IN VITRO ASSESSMENT OF BLACK AND GREEN TEA EFFECTS ON THE CORROSION AND MECHANICAL INTEGRITY OF ORTHODONTIC WIRES
Authors
Wurood khairallah Al-Lehaibi, Abdulrahman Al-Najjar, Faehaa Al-Mashhadane
Source journal
Bulletin of Stomatology and Maxillofacial Surgery
Published
2025-09-12
Licence
Creative Commons Attribution-NonCommercial 4.0 International
Original
https://doi.org/10.58240/1829006X-2025.21.8-340

Abstract

This in vitro study evaluated the comparative influence of black tea (5%) and green tea (3%) on the corrosion resistance and mechanical integrity of stainless steel (SS) and nickel titanium (NiTi) orthodontic wires. Sixty standardized specimens were immersed in tea solutions or distilled water over 28 days, simulating daily intake cycles. Surface morphology (SEM), elemental composition (EDX), tensile strength (Instron), surface roughness (profilometry), and corrosion potential (potentiostat) were assessed. Data were analyzed with one-way ANOVA followed by Tukey’s post hoc test (p≤0.05). Black tea exposure produced significantly greater deterioration than green tea. In SS wires, chromium content decreased markedly (18.0% → 17.2%), tensile strength was reduced by 12.5%, surface roughness increased to 0.51 µm, and corrosion potential dropped to –342 mV. NiTi wires exhibited milder yet statistically significant changes. Black tea accelerates electrochemical corrosion and mechanical deterioration of orthodontic wires more than green tea, particularly in stainless steel. These findings underscore the need for patient dietary counseling and suggest that protective coatings or antioxidant surface modifications could enhance the clinical longevity of orthodontic appliances.